Tensile Properties of Regenerated Bamboo Yarn

Research and development

Authors:

  • Li Long
    School of Textile & Materials, Xi’an Polytechnic University, Xi’an, P. R. China
  • Yan Hongqin (j/w)

Download... PDF
Full text

Abstract:

The tensile property of regenerated bamboo yarn of 14.58 tex was studied using an HD021N single yarn tensile tester at different tensile speeds (100, 500, 1000, 2000, 3000, 4000, and 5000 mm/min). It was observed that the distribution on diagrams of the breaking strengthfrequency and elongation at break frequency of yarn is normal. The breaking strength of the yarn increases when the tensile speed varies from 100 mm/min to 3000 mm/min, then the strength decreases greatly with an increase in tensile speed. The breaking time of the yarn decreases with an increase in tensile speed. A non-linear three-element viscoelastic model was used to simulate the tensile property of the yarn at various tensile rates. The relative error between the theoretical tenacity and actual tenacity is bound to be less than 3%.

Tags:

regenerated bamboo yarn, viscoelasticity, strength, tensile speed, modeling.

Citation:

Li, L.; Yan, H. Tensile Properties of Regenerated Bamboo Yarn. FIBRES & TEXTILES in Eastern Europe 2012, 20, 1(90) 20-22.

Published in issue no 1 (90) / 2012, pages 20–22.

CONTACT:

FIBRES & TEXTILES
in Eastern Europe
ul. Skłodowskiej-Curie 19/27,
90-570 Łódź, Poland
e-mail: infor@lit.lukasiewicz.gov.pl
ftee@lit.lukasiewicz.gov.pl
Events:

EDITORIAL OFFICE
FIBRES & TEXTILES in Eastern Europe 19/27 M. Skłodowskiej-Curie Str., 90-570 Łódź, Poland e-mail: infor@lit.lukasiewicz.gov.pl; ftee@lit.lukasiewicz.gov.pl

EDITORIAL DEPARTMENT
Editor-in-Chief Dariusz Wawro, Head of Editorial Office Janusz Kazimierczak, Text Editor Geoffrey Large, Assistant Editor Anna WahlProduction Łukasiewicz-ŁIT

facebook