Measurement of Joint Durability between an Aluminum Foil and Basalt Fabrics

Research and development

Authors:

  • Gilewicz Paulina
    Department of Clothing Technology and Textronics, Faculty of Material Technologies and Textile Design, Technical University of Lodz, Łódź, Poland
  • Frydrych Iwona
    Department of Clothing Technology and Textronics, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland
  • Frydrych Iwona
    Central Institute for Labour Protection - National Research Institute (CIOP-PIB), Łódź, Poland
  • Cichocka Agnieszka
    Department of Clothing Technology and Textronics, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland
  • Dominiak Justyna (j/w)
  • Hrynyk Rafał
    Central Institute for Labour Protection - National Research Institute (CIOP-PIB), Łódź, Poland
  • Orawiec Grażyna
    Department of Clothing Technology and Textronics, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland
  • Zieliński Janusz (j/w)

Nr DOI: 10.5604/01.3001.0013.4471

Download... PDF
Full text
Download... PDF
references

Abstract:

The aim of this paper was to determine the adhesion force between an aluminum foil and basalt fabrics. Aluminised basalt fabric can be used as an alternative solution for protective clothing production. So far aluminised glass fabric has been used for this purpose. The lamination of basalt fabrics with aluminum foil does not changed fabric flexibility and can provide better protection against thermal radiation. To check different variants of adhesion, fabrics reinforced by a steel wire were also used (wire diameter 0.1 mm). The steel wire caused an increase in the fabric tear strength as well as in puncture and cut resistance. Two types of glue were chosen to carry out an investigation on the strength of adhesive bonding (Butacoll A+ and Bonatex PU85). The adhesion strength of the laminates was measured according to the PN-88/P-04950 standard. The test results confirmed higher values for weft directions and the phenomenon of asymmetry of the bond strength was found during testing.

Tags:

 joint durability, aluminised basalt fabrics, lamination, glass fibres.

Citation:

Gilewicz P, Frydrych I, Cichocka A, Dominiak J, Hrynyk R, Orawiec G, Zieliński J. Measurement of Joint Durability between an Aluminum Foil and Basalt Fabrics. FIBRES & TEXTILES in Eastern Europe 2019; 27, 6(138): 81-84. DOI: 10.5604/01.3001.0013.4471

Published in issue no 6 (138) / 2019, pages 81–84.

CONTACT:

FIBRES & TEXTILES
in Eastern Europe
ul. Skłodowskiej-Curie 19/27,
90-570 Łódź, Poland
tel. (48-42) 638-03-14
tel. (48-42) 638-03-63
e-mail: infor@ibwch.lodz.pl

EDITORIAL OFFICE
ul. Skłodowskiej-Curie 1927, 90-570 Łódź, Poland • tel.  (48-42) 638-03-14 • e-mail: infor@ibwch.lodz.plhttp://www.fibtex.lodz.pl

EDITORIAL DEPARTMENT
Editor-in-Chief Emilia Jaszczurska-Niedźwiedzka, V-ce Editor-in-Chief Marta Cyrczak, Text Editor Geoffrey Large, Assistant Editor Anna Wahl, Typesetting and Printed at Media-Press • Production IBWCh

facebook