Zinc Alginate Fibres with a Tricalcium Phosphate (TCP) Nanoadditive

Research and development

Authors:

• Mikołajczyk Teresa
  Department of Spinning Technology and Yarn Structure, Technical University of Łódź, Łódź, Poland
• Boguń Maciej (j/w)
• Kurzak Andrzej (j/w)
• Szparaga Grzegorz
  Department of Man-Made Fibres, Faculty of Material Technologies and Textile Design, Technical University of Łódź, Łódź, Poland

Full text

Abstract: Conditions were found for the manufacture of zinc alginate fibres with a tricalcium phosphate (TCP) nanoadditive. The effect of essential forming process parameters were determined, such as temperature, solidification and plasticisation bath concentration, as well as as-spun draw ratio values for a porous structure and strength properties of nanocomposite zinc alginate fibres. A comparative analysis of the fibre properties with and without the nanoadditive was conducted.

Tags: alginate fibres, nano-additive, fibre forming, nanocomposite fibre properties

Citation: Mikołajczyk T., Boguń M., Kurzak A., Szparaga G.; Zinc Alginate Fibres with a Tricalcium Phosphate (TCP) Nanoadditive. FIBRES & TEXTILES in Eastern Europe 2009, Vol. 17, No. 2 (73), pp. 12-18.

Published in issue no 2 (73) / 2009, pages 12–18.